PHASE STABILITY AND IONIC CONDUCTIVITY OF NASICON-LIKE PHASES IN SCPO4-NA3PO4 - LI3PO4 TERNARY SYSTEM
Zhuravleva M.; Novoselov A.; Yoshikawa A.; Fukuda T.; Zakalyukin R.; Fomichev V.; Zimina G.
xmlui.dri2xhtml.METS-1.0.item-citation:Journal of Rare Earths, 2006, 24, Suppl., 162-165
Date:2006
Abstract:
Phase formation in ternary system of complex Sc, Na and Li phosphates was studied at 950°C and synthesis of new phases of definite composition was carried out. Obtained specimens were investigated with X-ray powder diffraction, infrared and impedance spectroscopy. Compositions of fields of homogeneity with NASICON-like structure were discovered. Temperature dependency of ionic conductivity was measured.