STRUCTURE OF HEAVY-METAL SORBED BIRNESSITE: PART 1. RESULTS FROM X-RAY DIFFRACTION

Abstract

The structure of heavy-metal sorbed synthetic birnessites (MeBi) was studied by powder X-ray diffraction (XRD) using a trial-and-error fitting procedure to improve our understanding of the interactions between buserite/birnessite and environmentally important heavy metals (Me) including Pb, Cd, and Zn. MeBi samples were prepared at different surface coverages by equilibrating at pH 4 a Na-rich buserite (NaBu) suspension in the presence of the desired aqueous metal. Two main types of experimental XRD patterns were obtained as a function of the nature of Me cations sorbed from solution which exerts a strong control on layer stacking sequence, as well as on location and coordination of Me: 1) CdBi and PbBi samples correspond to a one-layer hexagonal (1H) structure, AbCb'A' C'b'AbC..., and 2) ZnBi exhibits a one-layer monoclinic (1M) structure in which adjacent layers are shifted by +a/3, AbCb'A'c'BcAc'B'a'CaBa'C'b'AbC. Simulated XRD patterns shows that octahedral layers contain 0.833 Mn cations (Mn 4+ and Mn 3+) and 0.167 vacant octahedra; Mn3+ interlayer and adsorbed Meinterlayer compensate for the layer charge deficit. Mn 3+ interlayer is octahedrally coordinated in all samples and is located above or below vacant layer octahedra sharing three Olayer with neighboring Mnlayer octahedra to form a triple-corner surface complex ( VITC sites). In ZnBi and CdBi samples, Me interlayer is also located in TC sites; all Cd is octahedrally coordinated whereas about 30% of Zn is tetrahedrally coordinated ( IVTC sites). In PbBi samples, all Pb is octahedrally coordinated, most of these cations (~75%) being located in TC sites. Additional Pb is located above or below empty tridentate cavities, sharing three edges with neighboring Mnlayer octahedra ( VITE sites). Structural formulae calculated for each sample show that during the NaBu-to-MeBi structural transformation, interlayer Na + and Mn2+ are replaced by Me and H+ adsorbed from solution, whereas Mn 3+ interlayer resulting from the equilibration of NaBu at low pH is less affected. Sorption of divalent Me above and below vacant layer sites provides optimal conditions for local charge compensation in MeBi.