A TEMPERATURE-DEPENDENT SINGLE-CRYSTAL RAMAN SPECTROSCOPIC STUDY OF FAYALITE: EVIDENCE FOR PHONON-MAGNETIC EXCITATION COUPLING

Abstract

The polarized single-crystal Raman spectrum of synthetic fayalite, Fe2SiO4, was recorded between 5 and 773 K in order to investigate its lattice dynamic behavior. A broad absorption envelope is observed at wavenumbers between 800 and 960 cm−1 and it contains two intense bands at 816 and 840 cm−1 at 293 K in the (cc) spectrum. The integral area of the envelope decreases upon cooling from 293 K and reaches a minimum around 55 K. It then increases again with a further decrease in temperature down to 5 K. It is proposed that the envelope in the (cc) spectra consists of seven different modes, some of which are symmetry-forbidden, that arise from combination scattering of nonsymmetric internal SiO4-stretching modes of Big symmetry (i = 1, 2, 3) and low-energy excitations. The individual modes can be observed under different polarizations and agree in number and wavenumber with those obtained by fitting the broad envelope with Lorentzians. An analysis of the Raman spectrum as a function of temperature, using the known magnetic properties of fayalite, allows the assignment of the low-energy excitations to short-range magnetic interactions. Modulation of the Fe2+(1)–Fe2+(2) exchange energy leads to phonon-magnetic excitation coupling and the main role in the Fe2+(1)–Fe2+(2) magnetic interaction occurs via superexchange through the oxygens. The magnetic excitations are not magnons in the usual sense, that is as quasiparticles having a long wavelength in an ordered system. The degree of observed broadening of the SiO4-stretching modes is consonant with a Fe2+(1)–Fe2+(2) exchange energy of 4.7 cm−1 presented by Schmidt et al. (1992). At temperatures above 300 K the line width of the mode at 840 cm−1 decreases slightly, whereas those of low energy lattice modes increase. This suggests that a decrease in mode broadening due to weakened magnetic interactions compensates any thermally related broadening. Complete Fe2+ spin disorder may not be reached until at least 530 K. Results from this study show that estimates of third-law entropies for silicates using simple crystal-chemical considerations that do not account for magnetic properties cannot give accurate values for many transition-metal-containing phases.